Graphite electrode
![](/Content/pixel.gif)
RP Graphite Electrode | ||||||||
Item | Classification | Unit | Nominal Diameter(mm) | |||||
75-200 | 250-350 | 400-600 | ||||||
A grade | B grade | A grade | B grade | A grade | B grade | |||
Electric resistance(≯) |
Pole | μΩm | 8.0 | 9.0 | 8.0 | 9.0 | 8.0 | 9.0 |
Nipple | 6.0 | 6.0 | 6.0 | |||||
Bending strength(≮) |
Pole | Mpa | 10.0 | 9.0 | 8.0 | |||
Nipple | 15.0 | 15.0 | 15.0 | |||||
Young's modulus(≯) |
Pole | Gpa | 9.0 | 9.0 | 9.0 | |||
Nipple | 14.0 | 14.0 | 14.0 | |||||
Bulk density(≮) |
Pole | g/cm3 | 1.58 | 1.58 | 1.58 | |||
Nipple | 1.72 | 1.72 | 1.72 | |||||
(100℃-600℃) CTE(≯) |
Pole | x10-6/℃ | 2.7 | 2.7 | 2.7 | |||
Nipple | 2.5 | 2.5 | 2.5 | |||||
Ash content(≯) | Pole | % | 0.3 | 0.3 |
0.3 |
HP Graphite Electrode | |||||||
Item
|
Classification |
Unit
|
Nominal Diameter(mm) | ||||
HP | TYPEⅡHP | ||||||
200-400 | 450-500 | 550-700 | 350-400 | 450-600 | |||
Electric resistance(≯)
|
Pole | μΩm | 6.5 | 6.5 | 6.5 | 6.0 | 6.0 |
Nipple | 5.0 | 5.0 | 5.0 | 4.8 | 4.8 | ||
Bending strength(≮)
|
Pole | Mpa | 10.5 | 10.0 | 10.0 | 10.0 | 10.0 |
Nipple | 17.0 | 17.0 | 17.0 | 19.0 | 19.0 | ||
Young's modulus(≯)
|
Pole | Gpa | 12.0 | 12.0 | 12.0 | 14.0 | 14.0 |
Nipple | 16.0 | 16.0 | 16.0 | 18.0 | 18.0 | ||
Bulk density(≮)
|
Pole | g/cm3 | 1.65 | 1.65 | 1.65 | 1.66 | 1.66 |
Nipple | 1.76 | 1.76 | 1.76 | 1.77 | 1.77 | ||
(100℃-600℃) CTE(≯)
|
Pole | x10-6/℃ | 2.4 | 2.4 | 2.4 | 2.2 | 2.2 |
Nipple | 2.2 | 2.2 | 2.2 | 1.6 | 1.6 | ||
Ash content(≯) | Pole | % | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 |
Note:CTE and ash contents are only for reference |
UHP Graphite Electrode | ||||||
ItemClassification
|
Classification |
Unit
|
Nominal Diameter(mm) | |||
300-400 | 450-500 | 550-600 | 650-700 | |||
Electric resistance(≯)
|
Pole | μΩm | 6.0 | 5.8 | 5.5 | 5.0 |
Nipple | 4.8 | 4.5 | 4.2 | 4.0 | ||
Bending strength(≮)
|
Pole | Mpa | 10.5 | 10.5 | 10.0 | 10.0 |
Nipple | 20.0 | 20.0 | 23.0 | 24.0 | ||
Young's modulus(≯)
|
Pole | Gpa | 14.0 | 14.0 | 14.0 | 14.0 |
Nipple | 18.0 | 18.0 | 22.0 | 22.0 | ||
Bulk density(≮)
|
Pole | g/cm3 | 1.68 | 1.68 | 1.70 | 1.72 |
Nipple | 1.78 | 1.78 | 1.80 | 1.82 | ||
(100℃-600℃) CTE(≯)
|
Pole | x10-6/℃ | 1.5 | 1.5 | 1.4 | 1.4 |
Nipple | 1.4 | 1.4 | 1.2 | 1.2 | ||
Ash content(≯) | Pole | % | 0.3 | 0.3 | 0.3 | 0.3 |
Note:CTE and ash contents are only for reference |